In material science, amorphous is a solid whose internal microstructure lacking of long-range order that is characteristic of a crystal.
Amorphous is also called metallic glass.
After metal becomes amorphous, a subsequent heat treatment transforms the initially amorphous microstructure into new form in which fine crystalline grains (average grain diameter of 10-40 nm) embedded in an amorphous residual phase. The new form is called nanocrystalline.
SUNBOW’s iron-based amorphous alloy-SWAM is a product series which are universal solutions in many aspects to commonly use ferrite, silicon steel and iron powder materials, such as: power transformer, inductor, reactor, rotor & stator...
SUNBOW’s iron-based nanocrystalline alloy-SWNA is a product series which are excellent solutions to current transformer (high-precision for electricity meter, high-voltage for substation, and zero-sequence for leakage protection), high-frequency power transformer, and common mode choke (CMC) ...
Â
Manufacturing of SWAM & SWNA
Â
SUNBOW’s amorphous-SWAM & nanocrystalline-SWNA alloys are based on Fe, Si, B and with further additions of Nb and Cu, and produced by rapid solidification technology.
Composition metals melt in furnace under around 1500℃, and turn into liquid metal which pass through a narrow nozzle, and solidify at a rate of approximately 1million degrees/s. Atoms have no enough time to reach microstructure-crystalline state and stay in amorphous state.
A subsequent heat treatment-annealing at around 500~600℃ transforms the initially amorphous microstructure into nanocrystalline state in which fine crystalline grains (average grain diameter of 10-40 nm) embedded in an amorphous residual phase.
Â
Fig.1 Rapid solidification technology to produce thin metal ribbons with amorphous structure.
Â
Â
• The below characteristics of the iron-based amorphous alloys lead to ultra low core loss.
Thinner thickness —1/10 of CRGO;
Higher electrical resistance — two times higher than CRGO;
Lower coercive force —1/3 of CRGO.
• The magnetic devices made with iron-based amorphous alloy could be operated at higher working induction with excellent anti-saturate ability and smaller size, due to the highest saturation induction among all amorphous alloys.
• 3 tailored products of low core loss, excellent overload tolerance, and high saturation could be provided, according to customer’s different requirements.
Â
Â
SWAM
RIBBON MATERIAL
Â
Composition
Fe: 80%, Si: 9%, B: Balance
Â
Main Properties
Low coercivity-2.4 A/m Very high electrical resistivity-1.3 μΩ.m
Â
Applications
Power Transformer, High Speed Motor, Welding Machine, Medical Equipment (X-ray, CT, Nano-Knife)…
Â
Magnetic Properties (typical values)
Coercivity
|
2.4
|
A/m
|
Curie temperature
|
410
|
℃
|
Saturation flux density
|
1.56
|
T
|
Maximum permeability
|
200,000
|
Â
|
Initial permeability
|
1,000
|
Â
|
Saturation magnetostriction
|
20~30
|
ppm
|
Â
Static virgin curve (typical values)
Magnetic field strength
|
H (A/m)
|
3
|
100
|
500
|
1000
|
2000
|
3000
|
Induction
|
B (T)
|
0.6
|
0.7
|
0.75
|
1.2
|
1.5
|
1.56
|
Â
Iron Loss-B=0.1T (typical values)
Thickness
|
d (mm)
|
24
|
24
|
24
|
24
|
24
|
24
|
Frequency
|
f (KHz)
|
1.5
|
5.0
|
10
|
50
|
80
|
100
|
Loss
|
p (W/kg)
|
0.2
|
0.9
|
2.3
|
20
|
37
|
50
|
Â
Physical Property
Density
|
7.2
|
g/cm3
|
Electrical resistivity
|
1.3
|
μΩ.m
|
Thermal expansional
|
4.7
|
ppm/℃
|
Crystallization temperature
|
535
|
℃
|
Â
Form (soft & bendable)
·Cold-rolled:
|
Thickness=18~30μm
|
Width=142/170/213mm
|
·Slitting-strip:
|
Thickness=18~30μm
|
Width=5~80mm
|
Â
Important Note:
Specific magnetic properties could be induced by a heat treatment process.
To achieve optimum properties, a final annealing is indispensable!
Â
Â
Q: Are you trading company or manufacturer?
A: We are professional manufacturer specialized in the designã€development and production of new-type amorphousã€nanocrystallineã€silicon steel sheets and other magnetic materials and components.
Â
Q: What’s your production capacity?
A: The annual production capacity of amorphous&nanocrystalline ribbon is 600 tons;
The annual production capacity of power electronic core is 35 million;
C-type iron core annual production capacity of 240 tons;
The annual production capacity of reactors is 50,000;
Â
Â
Â
Three steps to start your customization today!
Â
1. Tell us what you need,you can call 021-63306968
Or send email to :sales@sunbowgroup.com
We supply nanocrystaline Soft Magnetic Material &Amorphous Soft Magnetic Material , please advise your request information:
1. Material Type
2. Application - Current Transformer, CMC, Audio, etc.?
3. Strips Width
4. Srips Thickness-- µm?
5. Potential Quantity -- kg?
Â
2. Get solution & quote
We will work on the best solution and provide primarily specification& quote for your review.
Â
3. Sample production and mass production
We will start mass production after customer confirmation and validation of samples.
Â
Â
Â
Â
Â
Â
Â
Â
Â
Â
Â
Â
Â
http://www.sunbowmagnetic.com/